Q345D seamless steel pipe

-

How to ensure the balance of performance of Q345D seamless steel pipe 


As we all know, Q345D seamless steel pipes are relatively easy to appear some problems in the production process. Katalor is a professional Q345D seamless steel pipe supplier in China, we only produce the Q345D seamless steel pipe with different sizes and high quality.

In order to ensure the performance homogenization of Q345D seamless steel pipes, we need to strictly control the annealing temperature, heat preservation time and cooling speed of Q345D seamless steel pipes. 

(1) Strictly control the annealing temperature of Q345D seamless steel pipes. When the annealing temperature is too high, the carbides dissolve more, the austenite homogenization degree is large and the core of the spheroidizing will be reduced or lost. The sheet like pearlite is easily obtained after the annealing of the Q345D seamless steel pipe; the temperature is too low, the original lamellar pearlite is difficult to dissolve, and the spheroidizing object can not be reached.

(2) Precise control of cooling speed. The cooling rate of spheroidizing annealing does not affect the shape of pearlite, but determines the dispersion of carbides, thus determining the hardness after annealing. When the cooling rate is too large and the carbide is not enough to gather and grow, the Q345D seamless steel pipe will produce a new crystal nucleus in the cooling, thus the fine granular or dot like pearlite with large dispersion can be obtained, and the hardness will be high. On the contrary, the coarse granular pearlite with a small dispersion and a low hardness is often obtained.

(3) Proper holding time of heat preservation. The long heat preservation time will lead to the homogenization of Q345D seamless steel pipe, which is not conducive to the spheroidization. When the time is too short, it is difficult to completely destroy the flake tissue in the original tissue, and can not achieve the effect of the spheroidization.

In order to control the Q345D seamless steel pipe quality, we have the professional team to produce Q345D seamless steel pipe. If you are interested in Q345D seamless steel pipe, please contact us for free. We can supply the Q345D seamless steel pipe with your requirements.

评论

发表评论

此博客中的热门博文

ASTM A517 steel belongs to the boiler steel plate

-
ASTM A517 steel (also called ASME SA517 standard) is a kind of high-strength quenched and tempered alloy steel plates intended for use in fusion welded boilers and other pressure vessels. The steel shall be killed and shall conform to the fine austenitic grain size requirement. Under this specification, the plate thickness determines the grade selection and the mechanical properties.   A517 grade A steel pates 2.5" in thickness and under, will have minimum Yield Strength of 100 ksi.  A517 grade b steel plates over 2.5" in thickness will have a minimum Yield strength of 90 ksi.  Typical applications include unfired vessels and tanks. ASTM A517 Grade A plates are Pressure Vessel Plate and supplied in the as-rolled condition. The ASTM A517 Gr. A plate may be ordered normalized or stress relieved, or both. ASTM A517 Grade H are Pressure Vessel Plate and supplied in the as-rolled condition. The ASTM A517 Gr. H Plate may be ordered normalized or stress relieved, or both. AS
阅读全文

20G boiler steel pipe

-
图片
Boiler operation status of the GB/T 5310 20G boiler steel pipe  Some steel companies produce the fake 20G boiler steel pipe cause the huge problems. Because the creep resistance of 20G boiler steel pipe is lower than other steel pipes and the 20G boiler steel pipe is overheated, the 20G boiler steel pipe wall metal overheated for a long time, which results in accelerated creep at high temperature, decreased strength, and finally the early creep burst occurred. During 20G boiler steel pipe fracture analysis, it was found that the macroscopic surface of the 20G boiler steel pipe fracture was covered with thin blue-purple oxide film, which indicated that the temperature of the 20G boiler steel pipe burst was 800℃, and the section was not smooth due to the effect of high temperature oxidation. There is a thick oxide layer on the inner surface of the  20G boiler steel pipe . The structure of the oxide layer has three layers and usually only when the ambient temperature
阅读全文

S235JR steel plate

-
图片
Katalor has more useful S235JR steel plate information S235JR steel plate  is a kind steel grade and it is mainly used for steel structural buildings, frames and other steel body under the standard of EN 10025-2.  S235JR steel plate  is for low temperature impacting test under zero centigree. Katalor steel Industrial specialized in S235JR steel plate  in china many decades years. The composition characteristics of S235JR steel plate  are low carbon, less than 0.20%, low alloy and total alloy element less than 3%. Low carbon content in S235JR steel plate  steel is to meet the technical requirements of plasticity, toughness, weldability and cold deformation of S235JR steel plate  used for engineering structural parts. The S235JR steel plate  has Mn as the main additive and conforms to the resource characteristics of our country. Mn not only has a significant strengthening effect on ferrite , but also reduces the cold and brittle temperature of the S235JR steel plate , and
阅读全文